| Product Description | |
|---|---|
| Supplier | Kingfa |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | |||
| 1 mm/min | 11000 | MPa | ISO 527-2 |
| tensile strength | |||
| 10 mm/min | 150 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 10 mm/min | 2.8 | % | ISO 527-2 |
| bending strength | |||
| 2 mm/min | 200 | MPa | ISO 178 |
| Bending modulus | |||
| 2 mm/min | 9000 | MPa | ISO 178 |
| Shore hardness | |||
| R-level | 120 | ISO 180 | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 9.0 | KJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 250 | ℃ | ISO 75-2 |
| 1.8 MPa | 220 | ℃ | ISO 75-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 10E+15 | ohm·cm | IEC 60093 |
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183-1 |
| Shrinkage rate | |||
| MD | 0.3 | % | ISO 2577 |
| TD | 0.9 | % | ISO 2577 |
| Water absorption rate | |||
| balance | 1.7 | % | ISO 62 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Processing temperature | Nominal value | Unit | Test method |
| The optimal temperature of the melt | 280 | ℃ | |
| Temperature at the rear of the barrel | 260 | ℃ | |
| Temperature in the middle of the barrel | 270 | ℃ | |
| Front temperature of material barrel | 275 | ℃ | |
| Mold temperature | 80 | ℃ | |
| Maximum processing temperature | 300 | ℃ | |
| Injection speed | 中等偏高 | ||
| drying temperature | 100-130 | ℃ | |
| Drying time | 4-6 | hr | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |