EcoVid 80TFH - SOLIAO

About
EcoVid-80TFH is a blend for thermoforming processes involving thin walled material with a High Heat resistance index. The material, rated for 178F/80°C and could be frozen to -32°C. Mould crystallization will increase the heat deflection from 80°C to 110°C+ depending on the application. Composition: Ingeo PLA content with bio-degradable and compostable HDT additives. Applications: EcoVid-80TFH is a Thermoforming blend suitable lids for hot coffee cups.&&

About

EcoVid-80TFH is a blend for thermoforming processes involving thin walled material with a High Heat resistance index. The material, rated for 178F/80°C and could be frozen to -32°C. Mould crystallization will increase the heat deflection from 80°C to 110°C+ depending on the application. Composition: Ingeo PLA content with bio-degradable and compostable HDT additives. Applications: EcoVid-80TFH is a Thermoforming blend suitable lids for hot coffee cups.&&

Product Description
Generic	PLA
Material Status	Commercial: Active
Features	Renewable resources,Biodegradable,High Heat Resistance
Availabilitys	North America,Europe
Process Methods	Thermo forming

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.27	g/cm³	ASTM D792
Melt Flow Rate			ASTM D1238
190℃，2.16kg	6.0	g/10min	ASTM D1238
210℃，2.16kg	6.0	g/10min	ASTM D1238
Shrinkage rate
MD	0.30 to 0.50	%
Relative viscosity	2.5

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	62.1	MPa	ASTM D638
Tensile strain
fracture	3.5	%	ASTM D638
bending strength	108	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	16	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Glass transition temperature	55.0 to 60.0	℃	ASTM D3418
Vicat Softening Temp	130	℃	ASTM D1525
Melting temperature	130 to 180	℃	ASTM D3418
Crystallization peak temperature
DSC	155 to 170	℃	ASTM D3418
Hot deformation temperature	80 to 110	℃	ASTM E2092

optical performance	Nominal value	Unit	Test method
Clarity	NIL

Process Conditions
injection	Nominal value	Unit	Test method
Hopper temperature	145 to 155	°C
Barrel rear temperature	145 to 165	°C
Barrel middle temperature	165 to 195	°C
Barrel front temperature	165 to 195	°C
Nozzle temperature	165 to 180	°C
Back pressure	1.03 to 2.76	MPa
Screw speed	35 to 65	rpm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.