| POLYSTYRENE (PS) COMPOUND (CPD) 828H is a high impact brominated flame retardant polystyrene for use use in HGW applications. PS CPD 828H can be supplied in both natural and coloured forms. Main Characteristics HBCD free Excellent UV stability Hot Glow Wire (HGW) rated to 850°C (*) High Flow Outstanding injectability Application Fuses boxes, Electrical Housings.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | PS (IRPS) |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,High liquidity,Halogen free,Flame Characteristics |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | < 1.13 | g/cm³ | ISO 1183 |
| Apparent density | 0.60 | g/cm³ | |
| Melt Flow Rate | |||
| 200℃，5.0kg | 15 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 2200 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 5.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 85.0 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Igniting temperature of the hot wire | |||
| 2 mm | 850 | ℃ | IEC 60695-2-13 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | < 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |