| UBE NYLON 5034 FDX40 is a high viscosity, nucleated Polyamide 6/6.6 copolymer. The material is suitable for cast film and air-cooled blown film production. Typical application is for shrink bags and pouches.&& |
| Product Description | |
|---|---|
| Supplier | UBE |
| Generic | PA66/6 |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good Clarity,High Viscosity,Nucleation,Low shrinkage |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.14 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| With oneself – dynamic | 1.0 | ASTM D1894 | |
| With oneself – static | 1.0 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | |||
| MD, cast thin film | 400 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, extruded film | 24.0 | MPa | ASTM D882 |
| MD, fracture, extruded film | 115 | MPa | ASTM D882 |
| Tensile strain | |||
| MD, fracture, extruded film | 650 | % | ASTM D882 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 197 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+15 | ohms | ASTM D257 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 155 | ASTM D523 | |
| Haze | < 0.50 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |