| About |
|---|
| ALCOM® PBT 700/12 PTFE10 is a Polybutylene Terephthalate (PBT) product filled with 10% ptfe fiber. It is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Characteristics include: RoHS Compliant Heat Resistant Wear Resistant&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | polybutylene terephthalate |
| Material Status | Commercial: Active |
| Features | Good liquidity,Good wear resistance,Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 20.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2400 | MPa | ISO 527-2 |
| tensile strength | 50.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 8.0 | % | ISO 527-2 |
| Bending modulus | 2470 | MPa | ISO 178 |
| bending strength | 80.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| — | 3.0 | kJ/m² | ISO 179/1eA |
| -40℃ | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| — | 52 | kJ/m² | ISO 179/1eU |
| -40℃ | 55 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 60.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 182 | ℃ | ISO 306 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | |||
| Desiccant desiccant | 100 to 120 | °C | |
| Hot air dryer | 100 to 120 | °C | |
| Drying time | |||
| Desiccant desiccant | 4.0 to 8.0 | hr | |
| Hot air dryer | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 250 to 270 | °C | |
| Mold temperature | 60 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |