| LCP-300/ LCP-270 is a high heat-resistance and anisotropic, Type I/ Type II grade Liquid Crystalline Polymer Compound LCP-300/LCP-270 appears low viscosity and high fluidity while operating temperature is higher than its melting point.&& |
| Product Description | |
|---|---|
| Supplier | Chang Chun |
| Generic | 液态聚合物 |
| Material Status | Commercial: Active |
| Features | High liquidity,Low Viscosity,V-0 |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.61 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 150 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 15000 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 220 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 20 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 270 | ℃ | ISO 75-2/A |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 2 mm | > 13 | kV/mm | ASTM D149 |
| Arc resistance | 150 | sec | ASTM D495 |
| Compared to the leakage tracing index | 125 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 140 | °C | |
| Drying time | 4.0 | hr | |
| Barrel rear temperature | 300 to 320 | °C | |
| Barrel middle temperature | 320 to 340 | °C | |
| Barrel front temperature | 340 to 360 | °C | |
| Nozzle temperature | 340 to 360 | °C | |
| Mold temperature | 40 to 120 | °C | |
| Injection pressure | 98.1 to 137 | MPa | |
| Hold pressure | 29.4 to 68.6 | MPa | |
| Back pressure | 0.800 to 1.00 | MPa | |
| Screw speed | 40 to 120 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |