| About |
|---|
| Hepla ® H7210GF FR is a Polyamide 66 (Nylon 66) product filled with 10% glass fiber.Characteristics include: Flame Retardant,Hot Water Moldability,Low Warpage,UV Stabilized. |
| Product Description | |
|---|---|
| Supplier | NFD |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Low CLTE,High impact resistance,Fatigue resistance,Insulation |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.20 mm | 0.4 to 0.6 | % | ASTM D955 |
| Water absorption rate | 0.8 | % | ASTM D570 |
| 24 hrs，23℃ | |||
| water content | 0.2 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| Tensile modulus | 5623 | MPa | ASTM D638 |
| tensile strength | 90.2 | MPa | ASTM D638 |
| Tensile strain | 3 to 4 | % | ASTM D638 |
| Bending modulus | 4795 | MPa | ASTM D790 |
| bending strength | 137.5 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.20 mm | 52.8 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 427 | J/m | ASTM D4812 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| In oil | 19.8 | kV/mm | ASTM D149 |
| Dielectric constant | 4 | ASTM D150 | |
| 1 MHz, dry | |||
| Dissipation factor | 0.017 | ASTM D150 | |
| 1 MHz, dry | |||
| Volume resistivity | >1E15 | Ohmcm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| Flame retardant level | |||
| 0.8mm | V-0 | UL94 | |
| 0.5mm | V-0 | UL94 | |
| Extreme oxygen index | 34 | % | ASTM D2863 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8MPa | 204 | ℃ | ASTM D648 |
| 0.45MPa | 216 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| Processing technology | Nominal value | Unit | Test method |
| Injection pressure | 70 to 125 | MPa | |
| Melt Temperature | 275 to 301 | ℃ | |
| Mold temperature | 65 to 108 | ℃ | |
| drying temperature | 79 | ℃ | |
| Drying time | 4 | hr | |
| Dew point temperature | -18 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |