| About |
|---|
| LNP™ STAT-KON™ UC1200 is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications. |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | Polyetherimide |
| Material Status | Commercial: Active |
| Features | Electrostatic discharge protection,High Heat Resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 337℃，6.6kg | 7.5 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.12 to 0.22 | % | |
| TD：3.2 mm | 0.30 to 0.50 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8130 | MPa | ASTM D638 |
| Tensile strength | |||
| yield | 131 | MPa | |
| fracture | 131 | MPa | |
| Tensile strain | |||
| yield | 5.1 | % | |
| fracture | 5.1 | % | |
| Bending modulus | |||
| 50 mm span | 7830 | MPa | |
| 100 mm span | 8270 | MPa | |
| bending strength | |||
| Fracture, 50 mm span | 221 | MPa | |
| Fracture, 100 mm span | 193 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 37 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 420 | J/m | ASTM D4812 |
| Dart impact equipped with measuring instruments (23 ° C, Total Energy) | 6.00 | J | ASTM D3763 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 3.2 mm | 213 | ℃ | |
| 1.8 MPa, unannealed, 3.2 mm | 208 | ℃ | |
| 1.8 MPa, unannealed, 6.4 mm | 210 | ℃ | |
| Vicat Softening Temp | 214 | ℃ | ASTM D1525 5 |
| Linear coefficient of thermal expansion | |||
| MD：-40~40℃ | 1.4E-5 | 1/℃ | |
| MD：-20~150℃ | 1.4E-5 | 1/℃ | |
| TD：-40~40℃ | 3.2E-5 | 1/℃ | |
| TD：-20~150℃ | 4.0E-5 | 1/℃ | |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.0E+5 | ohms | ASTM D257 |
| Volume resistivity | 4.0E+2 | ohms·cm | ASTM D257 |
| High Arc Burning Index (HAI) | PLC 2 | UL 746 | |
| Hot wire ignition (HWI) | PLC 2 | UL 746 | |
| Static Decay – 5000V to <50V | < 10 | msec | FTMS 101B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.60 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 150 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Suggested injection volume | 40 to 60 | % | |
| Temperature at the rear of the barrel | 360 to 405 | °C | |
| Temperature in the middle of the barrel | 370 to 420 | °C | |
| Front temperature of material barrel | 380 to 425 | °C | |
| Nozzle temperature | 375 to 420 | °C | |
| Processing (melt) temperature | 380 to 425 | °C | |
| Mold temperature | 135 to 165 | °C | |
| Back pressure | 0.300 to 0.700 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Exhaust hole depth | 0.025 to 0.076 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |