| About |
|---|
| Skived Ultra High Molecular Weight Polyethylene film (UHMW) UHMW has extremely high abrasion resistance, exceeding the abrasion resistance of steel. This coupled with broad chemcial resistance and low coefficient of friction makes UHMW an extremely versatile engineering material for many severe service applications. Application examples include inner and outer surfaces for potable water, chemical, fule and hydraulic hoses, bottom surfaces for skis and snow boards as well as linings for chutes to decrease friction and wear. Automotive weather stripping.&& |
| Product Description | |
|---|---|
| Generic | Ultra-high molecular weight polyethylene |
| Material Status | Commercial: Active |
| Features | Low coefficient of friction,Ultra high molecular weight,Good Tensile Strength,Good wear resistance,Solvent resistance |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | |
| Water absorption rate | |||
| saturated | 0.010 | % | |
| Thickness | 0.0762 to 2.36 | mm | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| MD, yield | 41.4 | MPa | ASTM D882 |
| Tensile strain | |||
| MD, fracture | 300 | % | ASTM D882 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 95.0 | ℃ | ISO 75-2/A |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-4 | 1/℃ | |
| Thermal conductivity coefficient | |||
| 23℃ | 0.063 | W/m/K | ASTM C177 |
| deformation | |||
| 50℃ | 6.0 to 8.0 | % |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 39 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 1 MHz | 2.30 | ASTM D150 | |
| Dissipation factor | 4.0E-4 | ASTM D150 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Core ID | 7.62 | cm | |
| Maximum Roll OD | 356 | mm | |
| Width | 6.35 to 1220 | mm |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2000 psi, 6 hr |
| 3. 2H |
| 4. (increments of 1/16″) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |