| About |
|---|
| LDPE FE 8000 is a low density polyethylene produced by a high pressure autoclave process. This grade is particularly suitable for transparent thin film. LDPE FE 8000 is suited to many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, lamination and coextrusion film.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Low density |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 40 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, yield, 40 µ m, blow molded film | 12.0 | MPa | ISO 527-3 |
| TD, yield, 40 µ m, blow molded film | 12.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 27.0 | MPa | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 23.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 40 µ m, blow molded film | 370 | % | ISO 527-3 |
| TD, fracture, 40 µ m, blow molded film | 570 | % | ISO 527-3 |
| Drop hammer impact | |||
| 40 µ m, blow molded film | 120 | g | ISO 7765-1 |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 40 µ m, blow molded film | 53 | N | ISO 6383-2 |
| TD: 40 µ m, blow molded film | 47 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 99.0 | ℃ | ISO 306 |
| Melting temperature | 111 | ℃ | ISO 11357-3 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 40 µ m, blow molded film | 11 | % | ISO 14782 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 160 to 200 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |