| SABIC® LDPE 2501N0 is a grade without additives with a low gel level, which combines good draw down ability with fair optical properties and stiffness. Application Blown Film: SABIC® LDPE 2501N0 is typically used in diaper film, surface protection film, lamination film and in applications where low blocking behaviour is required and the presence of slip and anti block is unwanted. Cast Film: SABIC® LDPE 2501N0 is typically used in diaper film, lamination film and in applications where low blocking behaviour without the help of additives is required. This product is not intended for and must not be used in any pharmaceutical/medical applications.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good dissection,Optical performance,Low speed solidification point,Low density |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.925 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.75 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | 0.90 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | |||
| — | 25 | µm | |
| — | 50 | µm | |
| Elastic modulus | |||
| TD, 50 µ m, blow molded film | 200 | MPa | ASTM D882 |
| MD, 50 µ m, blow molded film | 200 | MPa | ASTM D882 |
| Tensile modulus | ISO 527-3 | ||
| MD, 25 µ m, cast thin film | 150 | MPa | ISO 527-3 |
| TD, 25 µ m, cast thin film | 160 | MPa | ISO 527-3 |
| tensile strength | |||
| MD, yield, 50 µ m, blow molded film | 12.0 | MPa | ASTM D882 |
| TD, yield, 50 µ m, blow molded film | 12.0 | MPa | ASTM D882 |
| MD, yield, 25 µ m, blow molded film | 10.0 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 9.00 | MPa | ISO 527-3 |
| MD, fracture, 50 µ m, blow molded film | 25.0 | MPa | ASTM D882 |
| TD, fracture, 50 µ m, blow molded film | 20.0 | MPa | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 28.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 18.0 | MPa | ISO 527-3 |
| Tensile strain | |||
| MD, fracture, 50 µ m, blow molded film | > 200 | % | ASTM D882 |
| TD, fracture, 50 µ m, blow molded film | > 500 | % | ASTM D882 |
| MD, fracture, 25 µ m, cast thin film | 160 | % | ISO 527-3 |
| TD, fracture, 25 µ m, cast thin film | 580 | % | ISO 527-3 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod notched impact strength | ASTM D4272 | ||
| 50 µ m, blow molded | 150 | J/cm | ASTM D4272 |
| Cast thin film: 25.0 µ m | 140 | J/cm | ASTM D4272 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 98.0 | ℃ | ISO 306/A |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | ASTM D1003A | ||
| 50 µ m, blow molded film | 10 | % | ASTM D1003A |
| 25 µ m, cast thin film | 5.8 | % | ASTM D1003A |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blocking force | |||
| Blow molded film, 50.0 µ m | 20 | g | Internal Method |
| Re blocking – blow molded film (50.0 µ m) | < 5.0 | g | Internal Method |
| tear strength | ISO 6383-2 | ||
| MD，50 µm | 45.0 | kN/m | ISO 6383-2 |
| TD，50 µm | 45.0 | kN/m | ISO 6383-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Cast Film |
| 3. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |