| About |
|---|
| EDF-226A is a certified prime grade 6% ETHYLENE VINYL ACETATE (EVA) copolymer often used in the production of specialty films needing excellent heat sealability and impact strength. EDF-226A applications include freezer film, produce bags and films requiring good clarity. EDF-226A contains No slip and No antiblock. A melt temperature of 400°F or less is recommended to reduce the risk of polymer decomposition.&& |
| Product Description | |
|---|---|
| Generic | EVA |
| Material Status | Commercial: Active |
| Features | Good Clarity,High impact resistance,Food contact compliance,Copolymer,Heat Stabilized |
| Availabilitys | North America,Latin America |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| Vinyl acetate content | 6.0 | wt% | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 38 | µm | |
| tensile strength | ASTM D882 | ||
| MD, fracture, 38 µ m | 28.0 | MPa | ASTM D882 |
| TD, fracture, 38 µ m | 26.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 38 µ m | 350 | % | ASTM D882 |
| TD, fracture, 38 µ m | 650 | % | ASTM D882 |
| Drop hammer impact | |||
| 38 µm | 170 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：38 µm | 140 | g | ASTM D1922 |
| TD：38 µm | 100 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 102 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 38 µm | 2.5 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | < 204 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. F50 |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |