Quadrant EPP Nylatron® NSM

About
Quadrant EPP Nylatron® NSM is a Polyamide 6 (Nylon 6) product. It can be processed by casting and is available in Latin America or North America. Characteristics include: Flame Rated Lubricated&&

Product Description
Supplier	Quadrant
Generic	PA6
Material Status	Commercial: Active
Features	Good wear resistance,Lubricating,HB
Availabilitys	Europe

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	3.5	kJ/m²	ISO 179-1/eA
Charpy Unnotch Impact strength	75	kJ/m²	ISO 179-1/1eU

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa	75.0	℃	ISO 75-1/-2
Melting temperature
DSC， 10 ℃/min	215	℃	ISO 11357-1/-3
Linear coefficient of thermal expansion
MD
23 to 60 ℃	8.0E-5	m/(m·K)
23 to 100 ℃	9.5E-5	m/(m·K)
Thermal conductivity coefficient
23℃	0.29	W/m/K
Minimum operating temperature	-30	℃
Maximum operating temperature
Continuous 20000 hours	90	℃
Continuous 5000 hours	105	℃
short-term	165	℃

Electrical performance	Nominal value	Unit	Test method
Surface resistivity
23℃	> 1.0E+13	ohm/sq	IEC 60093
23°C，50%RH	> 1.0E+12	ohm/sq	IEC 60093
Volume resistivity
23℃	> 1.0E+14	ohm·cm	IEC 60093
23°C，50%RH	> 1.0E+12	ohm·cm	IEC 60093
Dielectric strength
1 mm in oil	25	kV/mm	IEC 60243-1
23 ° C, 50% RH, 1 mm, in oil	17	kV/mm	IEC 60243-1
Relative permittivity
100 Hz	3.60		IEC 60250
23°C，50%RH，100 Hz	6.60		IEC 60250
1 MHz	3.20		IEC 60250
23°C，50%RH，1 MHz	3.70		IEC 60250
Dissipation factor
100 Hz	0.012		IEC 60250
23°C，50%RH，100 Hz	0.14		IEC 60250
1 MHz	0.016		IEC 60250
23°C，50%RH，1 MHz	0.05		IEC 60250
Compared to the leakage tracing index	600		IEC 60112

FLAME CHARACTERISTICS	Nominal value	Test method
Flame retardant level
3.00 mm	HB	UL 94
6.00 mm	HB	UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
M-grade, 10.00 mm	81		ISO 2039-2
Ball hardness
10.0 mm	150	N/mm²	ISO 2039-1
Tensile modulus
23℃，1 mm/min	3150	MPa	ISO 527-1/-2
23℃，50%RH，1 mm/min	1525	MPa	ISO 527-1/-2
tensile strength
23℃，50 mm/min	80.0	MPa	ISO 527-1/-2
Tensile strain
23 ℃, 50 mm/min, yield	5.0	%	ISO 527-1/-2
23 ℃, 50 mm/min, fracture	25	%	ISO 527-1/-2
23 ℃, 50% RH, 50 mm/min, yield	＞50	%	ISO 527-1/-2
compressive strength
23 ℃, 1% strain	31.0	MPa	ISO 604
23 ℃, 2% strain	59.0	MPa	ISO 604
23 ℃, 5% strain	87.0	MPa	ISO 604
Tensile stress
23 ℃, 50 mm/min, yield	78	MPa	ISO 527-1/-2
23 ℃, 50% RH, 50 mm/min, yield	50	MPa	ISO 527-1/-2

Notes
1. Typical properties: these are not to be construed as specifications.
2. Method A (Short-Time)
3. 1-10, 1=Easier to Machine
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.