| KOPLA PA66 KUG1330BK是一种聚酰胺66（尼龙66）材料,含有的填充物为玻璃纤维增强材料。 该产品在亚太地区有供货,。 KOPLA PA66 KUG1330BK的主要特性为:阻燃/额定火焰。 典型应用领域包括: 电气/电子应用 汽车行业 工程/工业配件 罐子&& |
| Product Description | |
|---|---|
| Supplier | KOPLA |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 to 0.80 | % | ASTM D955 |
| Water absorption rate | |||
| 23℃，24hr | 0.70 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 140 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 255 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 250 | ℃ | ASTM D648 |
| Melting temperature | 260 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 3.0E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 25 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ASTM D785 | |
| tensile strength | |||
| Yield, 23 ℃ | 186 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.5 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 9320 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 265 | MPa | ASTM D790 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |