About
VENYL UE037 – 8139 is an unreinforced polyamide 66 with improved impact resistance intended for Injection moulding. APPLICATIONS VENYL UE037 – 8139 has been developed especially for very demanding applications in automotive industry and electrical parts requiring excellent combination between rigidity and high impact resistance at room temperature. It allows to avoid the conditioning of the part before use (low moisture absorption). VENYL UE037 – 8139 is available in both natural and other colours can be provided on request.&&

About

VENYL UE037 – 8139 is an unreinforced polyamide 66 with improved impact resistance intended for Injection moulding. APPLICATIONS VENYL UE037 – 8139 has been developed especially for very demanding applications in automotive industry and electrical parts requiring excellent combination between rigidity and high impact resistance at room temperature. It allows to avoid the conditioning of the part before use (low moisture absorption). VENYL UE037 – 8139 is available in both natural and other colours can be provided on request.&&

Product Description
Generic	PA66
Material Status	Commercial: Active
Features	Renewable resources,Low moisture absorption,HB
Availabilitys	Europe
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.10	g/cm³	ISO 1183
Shrinkage rate	1.6 to 2.3	%
Water absorption rate
Equilibrium, 23 ℃, 50% RH	2.2 to 2.4	%

MECHANICAL	Nominal value	Unit	Test method
Tensile modulus	2400	MPa	ISO 527-2
tensile strength
fracture	50.0 to 55.0	MPa	ISO 527-2
Tensile strain
yield	13 to 45	%	ISO 527-2
Bending modulus	1700 to 1900	MPa	ISO 178
bending strength	60.0 to 70.0	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Charpy Notched Impact Strength	80 to 85	kJ/m²	ISO 179
Charpy Unnotch Impact strength	No Break		ISO 179
Impact strength of cantilever beam notch	75 to 80	J/m	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	70.0	℃	ISO 75-2/A
0.45 MPa, unannealed	213	℃	ISO 75-2/B
Melting temperature
DSC	256	℃	ISO 3146

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+14	ohms	DIN 53482
Volume resistivity	1.0E+15	ohms·cm	DIN 53482
Compared to the leakage tracing index
Solution A	600	V	IEC 60112

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
1.60 mm	HB		UL 94
Extreme oxygen index	22	%	ISO 4589-2

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	80	°C
Drying time	4.0	hr
Barrel rear temperature	270 to 285	°C
Barrel middle temperature	265 to 280	°C
Barrel front temperature	260 to 275	°C
Nozzle temperature	260 to 275	°C
Mold temperature	75 to 85	°C
Injection pressure	60.0 to 90.0	MPa
Injection speed	Fast
Hold pressure	35.0 to 60.0	MPa
Screw length to diameter ratio	15.0:1.0 to 20.0:1.0

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.