UNIVAL™ DMDA-6147 NT 7

About
Outstanding environmental stress crack resistance Excellent parison melt strength/low sag Good extrudability/processability Good rigidity Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Complies with CANADIAN HPFB NO OBJECTION (WITH LIMITATIONS) Consult the regulations for complete details. UNIVAL™ DMDA-6147 NT 7 High Density Polyethylene (HDPE) Resin is a polymer with broad molecular weight distribution and high molecular weight. This product provides an excellent combination of extrudability and parison stability, which contribute to uniform wall thickness in large parts. UNIVAL DMDA-6147 NT 7 HDPE resin is ideal for blow molding containers such as the 5-55 gallon (19-212 liter) closed head shipping containers and other similar parts. The broad distribution also provides outstanding environmental stress crack resistance (ESCR) at a good rigidity. Because of these characteristics, a wide variety of products, such as industrial chemicals, latex paints, printing inks, foodstuffs, adhesives, and other chemical specialties may be packaged in containers produced from this resin. The smooth surface of molded parts is readily treated and printed for high quality applications.&&

About

Outstanding environmental stress crack resistance Excellent parison melt strength/low sag Good extrudability/processability Good rigidity Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Complies with CANADIAN HPFB NO OBJECTION (WITH LIMITATIONS) Consult the regulations for complete details. UNIVAL™ DMDA-6147 NT 7 High Density Polyethylene (HDPE) Resin is a polymer with broad molecular weight distribution and high molecular weight. This product provides an excellent combination of extrudability and parison stability, which contribute to uniform wall thickness in large parts. UNIVAL DMDA-6147 NT 7 HDPE resin is ideal for blow molding containers such as the 5-55 gallon (19-212 liter) closed head shipping containers and other similar parts. The broad distribution also provides outstanding environmental stress crack resistance (ESCR) at a good rigidity. Because of these characteristics, a wide variety of products, such as industrial chemicals, latex paints, printing inks, foodstuffs, adhesives, and other chemical specialties may be packaged in containers produced from this resin. The smooth surface of molded parts is readily treated and printed for high quality applications.&&

Product Description
Supplier	DOW
Generic	HDPE
Material Status	Commercial: Active
Availabilitys	North America

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.948	g/cm³	ASTM D792
Melt Flow Rate
190℃，21.6kg	10	g/10min	ASTM D1238
ESCR(Environmental Stress Cracking Resistance)
50 ℃, 100% non-ionic surfactant, F50	> 1500	hr	ASTM D1693

IMPACT	Nominal value	Unit	Test method
Tensile impact strength	462	kJ/m²	ASTM D1822

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	66.0	℃	ASTM D648
Embrittlement temperature	< -76.1	℃	ASTM D746
Vicat Softening Temp	127	℃	ASTM D1525
Melting temperature
DSC	130	℃	Internal Method
Crystallization peak temperature
DSC	114	℃	Internal Method

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	57		ASTM D2240
tensile strength			ASTM D638
yield	22.8	MPa	ASTM D638
fracture	36.5	MPa	ASTM D638
Tensile strain			ASTM D638
yield	6.0	%	ASTM D638
fracture	900	%	ASTM D638
Bending modulus
2% secant	855	MPa	ASTM D790-B

Notes
1. With limitations
2. Typical properties: these are not to be construed as specifications.
3. Type S
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.