| BPD2000E is an unstabilised and clean low density polyethylene. Applications BPD2000E is designed for use in Medium/High Voltage (MV/HV) power cables insulation using the direct peroxide injection (DPI) process and applications requesting extra cleanliness. Suitability of BPD2000E for insulation of HV cables and voltage limitation depend on experience acquired and validations undergone by the cable manufacturer.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | High purity,Low density |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Fracture, 23 ℃ | 18.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 500 | % | ISO 527-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | |||
| 23℃ | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | > 22 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 50 Hz | 2.30 | ASTM D150 | |
| Dissipation factor | |||
| 50 Hz | 3.0E-4 | ASTM D150 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 135 to 145 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |