| GE200C is a polyethylene based compatibilizer containing anhydride functionality. It is available in pellet form and designed for use in conjunction with a polar material(PA, metal, inorganic matter, etc.) and a polyethylene. GE200C has high physical properties originated from polyethylene and shows excellent adhesion strength and processibility.&& |
| Product Description | |
|---|---|
| Supplier | HYUNDAI EP |
| Generic | PE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good bond |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.80 | g/10min | ASTM D1238 |
| Maleic anhydride content | High | wt% | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 130 | ℃ | ASTM D3418 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Adhesive strength | > 2.0 | kN/m | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 67 | ASTM D785 | |
| tensile strength | |||
| yield | 22.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 700 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 150 to 160 | °C | |
| Barrel 2 zone temperature | 190 to 200 | °C | |
| Barrel 3 zone temperature | 200 to 210 | °C | |
| Barrel 4 zone temperature | 210 to 220 | °C | |
| Barrel 5 zone temperature | 220 to 230 | °C | |
| Nozzle temperature | 220 to 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |