Moplen HP422H - SOLIAO

About
Moplen HP422H is a modified polypropylene homopolymer designed for the production of BOPP films at very high speed. BOPP films produced with HP422H feature good mechanical properties, excellent barrier against moisture, odours, oxygen, good transparency and gloss. Coextruded films made of Moplen HP422H are widely used in the food packaging industry. Moplen HP422H does not contain any slip or antistatic agents and no Calcium Stearate is intentionally added.&&

About

Moplen HP422H is a modified polypropylene homopolymer designed for the production of BOPP films at very high speed. BOPP films produced with HP422H feature good mechanical properties, excellent barrier against moisture, odours, oxygen, good transparency and gloss. Coextruded films made of Moplen HP422H are widely used in the food packaging industry. Moplen HP422H does not contain any slip or antistatic agents and no Calcium Stearate is intentionally added.&&

Product Description
Supplier	LyondellBasell
Generic	PP homopolymerization
Material Status	Commercial: Active
Features	Good Clarity,Good surface appearance,Retention of aroma ,Low odor,Food contact compliance,Moisture resistance,Homopolymer
Availabilitys	Africa & Middle East ,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	2.0	g/10min	ISO 1133

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	88.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	152	℃	ISO 306/A50

optical performance	Nominal value	Unit	Test method
Haze
20 µm	0.50	%	ASTM D1003

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	70		ISO 868
Tensile modulus
—	1450	MPa	ISO 527-1-2
Tangent, 0.02 mm	2400	MPa	Internal Method
tensile strength
yield	34.0	MPa	ISO 527-2/50
Fracture, 0.02 mm	116	MPa	Internal Method
Tensile strain
yield	10	%	ISO 527-2/50
fracture	410	%	ISO 527-2/50
Fracture, 0.02 mm	29	%	Internal Method

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.