| About |
|---|
| Telcar TELC 1000-92 UV-2 BLACK 550 is a high hardness, low density high performance thermoplastic elastomer designed for various applications in the automotive and consumer/industrial segments. Telcar TELC 1000-92 UV-2 BLACK 550 has good UV resistance, good impact resistance and is suitable for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | TPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,High impact resistance,Good Hardness,Good bond,Low density,Solvent resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Shore hardness | ISO 868 | ||
| Shore D, 10 seconds | 42 | ASTM D2240 | |
| Shore D, 1 second | 49 | ISO 868 | |
| Shaw’s D, 5 seconds | 41 | ISO 868 | |
| Bending modulus | 290 | MPa | ASTM D790 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ISO 37 | ||
| fracture | 7.40 | MPa | ISO 37 |
| MD, fracture | 9.90 | MPa | ISO 37 |
| Tensile strain | ISO 37 | ||
| fracture | 370 | % | ISO 37 |
| Flow rate, fracture | 270 | % | ISO 37 |
| tear strength | |||
| TD | 87 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，22 hr | 60 | % | ISO 815 |
| 70℃，22 hr | 74 | % | ISO 815 |
| 90℃，70 hr | 93 | % | ISO 815 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -40℃ | No Break | ASTM D256 | |
| Drop hammer impact | |||
| -30℃ | 33.9 | J | ASTM D3029 |
| Tensile impact strength | 471 | kJ/m² | ASTM D1822 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 40.7 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 62.5 | ℃ | ASTM D648 |
| Glass transition temperature | -55.9 | ℃ | ASTM E1356 |
| Linear coefficient of thermal expansion | |||
| TD | 1.2E-4 | 1/℃ | ASTM D696 |
| MD | 1.2E-4 | 1/℃ | ASTM D696 |
| Aging performance | Nominal value | Unit | Test method |
|---|---|---|---|
| The rate of change in tensile strength in air | ASTM D573 | ||
| — | 6.0 | % | ASTM D573 |
| 110℃，1008 hr | 10 | % | ASTM D573 |
| 121℃，1008 hr | 7.0 | % | ASTM D573 |
| The rate of change in tensile strength in air | ISO 188 | ||
| 110℃，1008 hr | 1.6 | % | ISO 188 |
| 125℃，168 hr | 4.3 | % | ISO 188 |
| The rate of change in ultimate elongation in air | ASTM D573 | ||
| 110℃，1008 hr | -67 | % | ASTM D573 |
| 121℃，1008 hr | -63 | % | ASTM D573 |
| Changes in tensile stress during fracture in air | ISO 188 | ||
| 110℃，1008 hr | -43 | % | ISO 188 |
| 125℃，168 hr | -40 | % | ISO 188 |
| The rate of change of Shore hardness in air | |||
| Shore D, 110 ℃, 1008 hr | 1.7 | ISO 188 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | 30 | mm/min | ISO 3795 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Xenon aging test | |||
| Delta E 2500 kJ | 0.170 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 0.911 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 2.6 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD：180℃，30 min | 1.3 | % | ASTM D955 |
| MD：24 hrs | 1.1 | % | ASTM D955 |
| Apparent viscosity of melt | |||
| 200℃，206 sec^-1 | 516 | Pa·s | ASTM D3835 |
| Special value | Nominal value | Unit | Test method |
|---|---|---|---|
| TD, 100% strain | 7.02 | MPa | ISO 37 |
| MD, 100% strain | 9.60 | MPa | ISO 37 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 171 to 193 | °C | |
| Barrel middle temperature | 177 to 199 | °C | |
| Barrel front temperature | 182 to 204 | °C | |
| Nozzle temperature | 188 to 210 | °C | |
| Processing (melt) temperature | 188 to 210 | °C | |
| Mold temperature | 25 to 66 | °C | |
| Injection pressure | 1.38 to 6.89 | MPa | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 0.172 to 0.345 | MPa | |
| Screw speed | 50 to 100 | rpm | |
| Cushion | 3.81 to 25.4 | mm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |