| About |
|---|
| PTS- Creamid B3H2G10*9000是一种聚酰胺6（尼龙6）材料,。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 PTS- Creamid B3H2G10*9000的主要特性为:阻燃/额定火焰。 |
| Product Description | |
|---|---|
| Supplier | Teknor Apex |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.59 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.1 | % | |
| MD | 0.50 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.50 | % | |
| Saturation, 23 ℃ | 4.1 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 16600 | MPa | |
| Tensile stress (fracture) | 225 | MPa | |
| Tensile strain | |||
| fracture | 3.4 | % | |
| Bending modulus | |||
| 23℃ | 13700 | MPa |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 12 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 75 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| 23℃ | 12 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 220 | ℃ | |
| 1.8 MPa, unannealed | 215 | ℃ | |
| Vicat Softening Temp | |||
| — | 223 | ℃ | |
| — | 218 | ℃ | |
| Melting temperature | 222 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Nozzle temperature | 270 | °C | |
| Processing (melt) temperature | 255 to 275 | °C | |
| Mold temperature | 70 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |