ExxonMobil™ LLDPE LL 1001AV

About
ExxonMobil™ LLDPE LL 1001AV LL 1001AV offers excellent drawdown and puncture resistance combined with high gloss and clarity. It is frequently used as a blend partner with LDPE resins to improve film properties and processability. LL 1001AV is TNPP-free.&&ExxonMobil™ LLDPE LL 1001AV LL 1001AV is a C4 Ziegler Natta LLDPE for power cable and Telecom jacketing. The grade contains a low level of antioxidants and has excellent Environmental Stress Crack Resistance (ESCR). Sufficient Carbon Black or UV stabilizer should be added to meet cable jacketing specifications.&&

About

ExxonMobil™ LLDPE LL 1001AV LL 1001AV offers excellent drawdown and puncture resistance combined with high gloss and clarity. It is frequently used as a blend partner with LDPE resins to improve film properties and processability. LL 1001AV is TNPP-free.&&ExxonMobil™ LLDPE LL 1001AV LL 1001AV is a C4 Ziegler Natta LLDPE for power cable and Telecom jacketing. The grade contains a low level of antioxidants and has excellent Environmental Stress Crack Resistance (ESCR). Sufficient Carbon Black or UV stabilizer should be added to meet cable jacketing specifications.&&

Product Description
Supplier	ExxonMobil
Generic	Linear low density polyethylene
Material Status	Commercial: Active
Availabilitys	Africa & Middle East ,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.918	g/cm³	ExxonMobil Method
Melt Flow Rate
190℃，2.16kg	1.0	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
Secant modulus
1% secant, MD	200	MPa
1% secant, TD	220	MPa
tensile strength
MD, fracture	60.0	MPa
TD, fracture	36.0	MPa
Tensile strain
MD, fracture	570	%
TD, fracture	840	%
Drop hammer impact	90	g	ASTM D1709-A
Elmandorf tear strength
MD	80	g
TD	430	g

optical performance	Nominal value	Unit	Test method
gloss
45°	48		ASTM D2457
Haze	13	%	ASTM D1003

Legal Statement	Nominal value	Unit	Test method

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.