SEPAZ™ C130M

About
SEPAZ™ C130M是一种液晶聚合物（LCP）产品,含有的填充物为30% 矿物填料。它,在亚太地区有供货。主要特性为:阻燃/额定火焰。&&

Product Description
Supplier	Mando
Generic	液态聚合物
Material Status	Commercial: Active
Features	V-0
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.63	g/cm³	ASTM D792
Shrinkage rate			ASTM D955
MD	0.0	%
TD	0.50	%

MECHANICAL	Nominal value	Unit	Test method
tensile strength	127	MPa	ASTM D638
Tensile strain
fracture	4.0	%	ASTM D638
Bending modulus	9610	MPa	ASTM D790
bending strength	127	MPa	ASTM D790

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	239	℃	ASTM D648
Melting peak temperature	335	℃	ASTM D2133

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	> 1.0E+15	ohms	ASTM D257
Volume resistivity	> 1.0E+13	ohms·cm	ASTM D257
Dielectric strength
1.6 mm	26	kV/mm	ASTM D149
Dielectric constant	3.20		ASTM D150
Dissipation factor	0.028		ASTM D150

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	V-0		UL 94

Process Conditions
injection	Nominal value	Unit	Test method
Processing (melt) temperature	350 to 360	°C
Mold temperature	30.0 to 150	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.