| 25% glass fiber reinforced, impact modified and heat stabilized, recycled grade |
| Product Description | |
|---|---|
| Supplier | A. Schulman |
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.30 | g/cm³ | ISO 1183/A |
| Melt Volume Rate | 40.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.90 to 1.1 | % | |
| MD | 0.40 | % | |
| Water absorption rate | |||
| 23 ℃, in water | 5.5 | % | GE |
| Viscosity (96% H2SO4) | 155 | cm³/g | ISO 307 |
| Humidity Absorption – （23°C，50% R. H.） | 1.5 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 6800 | MPa | ISO 527-2/1A/1 |
| Tensile stress (fracture) | 140 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 3.5 | % | ISO 527-2/1A/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 75 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 250 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 235 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 245 | ℃ | ISO 306 |
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | HB | ||
| 1.60 mm | HB |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 80 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.040 to 0.10 | % | |
| Suggested maximum proportion of recycled materials | 20 | % | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 60 to 120 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |