| 15% GLASS FIBER REINFORCED, HEAT STABILIZED AND IMPACT MODIFIED P.E.T. FOR INJECTION MOULDING APPLICATION.&& |
| Product Description | |
|---|---|
| Supplier | Ram-On |
| Generic | PET |
| Material Status | Commercial: Active |
| Features | High impact resistance,Heat Stabilized,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ASTM D792 |
| Density | 1.38 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.15 to 0.30 | % | ISO 2577 |
| MD | 0.15 to 0.30 | % | ASTM D955 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.25 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.25 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 4500 | MPa | ASTM D638 |
| Tensile modulus | 4500 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 80.0 | MPa | ISO 527-2 |
| yield | 80.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.0 | % | ISO 527-2 |
| fracture | 4.0 | % | ASTM D638 |
| Bending modulus | 4000 | MPa | ASTM D790 |
| Bending modulus | 4000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 11 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 50 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | |||
| 23℃ | 10 | kJ/m² | ISO 180 |
| 23℃ | 100 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 187 | ℃ | ISO 75-2/A |
| 1.8 MPa, unannealed | 187 | ℃ | ASTM D648 |
| Melting peak temperature | 252 | ℃ | ASTM D3417 |
| Melting temperature | 252 | ℃ | ISO 11357-3 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |