| CYCOLAC DL200H is a hydrostable high heat ABS/PC blend&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,High Heat Resistance |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 260℃，5.0kg | 25 | g/10min | ASTM D1238 |
| 220℃，10.0kg | 9.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2330 | MPa | ASTM D638 |
| Tensile modulus | 2350 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 40.0 | MPa | ISO 527-2/50 |
| yield | 49.0 | MPa | ISO 527-2/50 |
| yield | 47.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 70 | % | ASTM D638 |
| fracture | 75 | % | ISO 527-2/50 |
| yield | 3.9 | % | ISO 527-2/50 |
| Bending modulus | 2100 | MPa | ISO 178 |
| 50 mm span | 2200 | MPa | ASTM D790 |
| bending strength | 75.0 | MPa | ISO 178 |
| bending strength | |||
| Yield, 50 mm span | 77.0 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 30 | kJ/m² | ISO 179/1eA |
| 23℃ | 65 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 620 | J/m | ASTM D256 |
| 23℃，6.4mm | 500 | J/m | ASTM D256 |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -40℃ | 21 | kJ/m² | ISO 180-1A |
| 23℃ | 56 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 1.8 MPa, unannealed, 64 mm span | 96.0 | ℃ | ISO 75-2/Af |
| 0.45 MPa, unannealed, 64 mm span | 120 | ℃ | ISO 75-2/Bf |
| 0.45 MPa, unannealed, 3.2 mm | 118 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 96.0 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 6.4 mm | 101 | ℃ | ASTM D648 |
| Vicat Softening Temp | |||
| B50 | 112 | ℃ | ISO 306 |
| B120 | 114 | ℃ | ISO 306/B120 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 99 to 104 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Drying time, maximum | 8.0 | hr | |
| Recommended maximum moisture content | 0.040 | % | |
| Recommended injection volume | 30 to 80 | % | |
| Barrel rear temperature | 249 to 282 | °C | |
| Barrel middle temperature | 254 to 288 | °C | |
| Barrel front temperature | 254 to 288 | °C | |
| Nozzle temperature | 260 to 288 | °C | |
| Processing (melt) temperature | 260 to 288 | °C | |
| Mold temperature | 77 to 99 | °C | |
| Back pressure | 0.345 to 0.689 | MPa | |
| Screw speed | 40 to 70 | rpm | |
| Vent depth | 0.038 to 0.076 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.20 in/min |
| 3. Type I, 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Yield |
| 7. 80*10*4 sp=62mm |
| 8. 80*10*4 |
| 9. 80*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |