| AKROLOY® PA GF 50 natural (6414) is a 50% glass fibre reinforced polyamide blend with very high stiffness and strength, even in conditioned state. Components with high dimensional stability, independent from moisture content. AKROLOY® PA GF 50 is an alternative for aluminium- and zinc diecast alloys.&& |
| Product Description | |
|---|---|
| Generic | PA 66+PA 6I/6T |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Dimensional Stability |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.56 | g/cm³ | ISO 1183 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 17000 | MPa | ISO 527-1-2 |
| tensile strength | |||
| fracture | 275 | MPa | ISO 527-2/5 |
| Tensile strain | |||
| fracture | 2.8 | % | ISO 527-2/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 110 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 245 | ℃ | ISO 75-2/A |
| 8.0 MPa, unannealed | 185 | ℃ | ISO 75-2/C |
| Melting temperature | 255 | ℃ | DIN EN 11357-1 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ash Content | 50 | % | ISO 1172 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |