| About |
|---|
| NORYL PX1134 is an unfilled material with a Vicat B/120 of 120?C according ISO 306. NORYL PX1134 offers improved impact performance to meet the standard ECE dashboard impact tests in the automotive industry. Available in several colours, which meet the various automotive standards for interior colours.&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PPO(PPE)+PS |
| Material Status | Commercial: Active |
| Features | High impact resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 280℃，5 kg | 10.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.50 to 0.70 | % | Internal Method |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.14 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.060 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 14 | kJ/m² | |
| 23℃ | 19 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 18 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 120 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 105 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| A50 | 130 | ℃ | ISO 306/A50 |
| B50 | 115 | ℃ | ISO 306 |
| B120 | 125 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 73~77℃ | 通过 | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | |||
| MD：23~80℃ | 7.0E-5 | 1/℃ | |
| TD：23~80℃ | 9.0E-5 | 1/℃ | |
| Thermal conductivity coefficient | 0.23 | W/m/K | ISO 8302 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3.2 mm in oil | 17 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 50 Hz | 2.70 | ||
| 60 Hz | 2.70 | ||
| 1 MHz | 2.60 | ||
| Dissipation factor | |||
| 50 Hz | 4.0E-4 | ||
| 60 Hz | 4.0E-4 | ||
| 1 MHz | 9.0E-4 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 80.0 | MPa | ISO 2039-1 |
| Tensile modulus | 2100 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 40.0 | MPa | |
| fracture | 40.0 | MPa | |
| Tensile strain | |||
| yield | 3.0 | % | |
| fracture | 40 | % | |
| Bending modulus | 1900 | MPa | ISO 178 |
| bending strength | 85.0 | MPa | ISO 178 |
| Taber abraser | |||
| 1000 cycles, 1000 g, CS-17 wheels | 65.0 | mg | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 100 to 120 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 240 to 260 | °C | |
| Barrel middle temperature | 260 to 280 | °C | |
| Barrel front temperature | 280 to 300 | °C | |
| Nozzle temperature | 260 to 280 | °C | |
| Processing (melt) temperature | 280 to 300 | °C | |
| Mold temperature | 80 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. at Yield |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*4 mm |
| 7. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |