| Custom Molding&& |
| Product Description | |
|---|---|
| Generic | PVC alloy |
| Material Status | Commercial: Active |
| Features | High liquidity |
| Availabilitys | Asia Pacific,Latin America,Europe,Africa & Middle East ,North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.27 | g/cm³ | ASTM D792 |
| Spiral flow length | 104 | cm | |
| Shrinkage rate | |||
| MD | 0.20 to 0.50 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 210 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.2 mm | 59.5 | ℃ | ASTM D648 |
| 0.45 MPa, annealed, 3.2 mm | 67.8 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed, 3.2 mm | 51.6 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm | 64.4 | ℃ | ASTM D648 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 80 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃，3.18 mm | 1910 | MPa | ASTM D638 |
| tensile strength | |||
| Yield, 23 ℃, 3.18 mm | 40.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃, 3.18 mm | 35 | % | ASTM D638 |
| Bending modulus | |||
| 23℃，3.18 mm | 1920 | MPa | ASTM D790 |
| bending strength | |||
| 23℃，3.18 mm | 57.2 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 199 to 204 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |