| EnvisionTEC’s D3 M material is a fast-growing, tough material with similar characteristics to ABS plastic. The material is ideal for quickly produced prototypes, client evaluation pieces and dental models. Applications Jewelry, MCAD, Dental/Orthodontic Recommended Machines: Perfactory® Micro EDU, Perfactory® Micro Ortho, Perfactory® Micro Advantage&& |
| Product Description | |
|---|---|
| Generic | SMMA |
| Material Status | Commercial: Active |
| Features | Good flexibility |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| IMPACT | Nominal value | Unit | Test method |
| Notched impact strength of cantilever beam | |||
| — | 24 | J/m | ASTM D256 |
| — | 2.5 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 83.0 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 80.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 50.8 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 48.9 | ℃ | ISO 75-2/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 88 | ASTM D2240 , ISO 868 | |
| Tensile modulus | 2590 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 28.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1.3 | % | ASTM D638 |
| Bending modulus | |||
| — | 1870 | MPa | ASTM D790 |
| — | 1880 | MPa | ISO 178-A |
| bending strength | |||
| — | 56.8 | MPa | ISO 178-A |
| fracture | 50.1 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |