| About |
|---|
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | HB |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 23℃ | 1.08 | g/cm³ | GB/T 1033 |
| Melt Flow Rate | |||
| 200℃, 5Kg | 14 | g/10min | GB/T 3682 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 50mm/min | 47 | Mpa | GB/T 1040 |
| Breaking elongation rate | |||
| 50mm/min | 20 | % | GB/T 1040 |
| bending strength | |||
| 2mm/min | 63 | Mpa | GB/T 9341 |
| Bending modulus | |||
| 2mm/min | 2100 | Mpa | GB/T 9341 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.2mm 23℃ | 420 | J/m | GB/T 1843 |
| 6.4mm 23℃ | 300 | J/m | GB/T 1843 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa | 103 | ℃ | GB/T 1634 |
| Vicat Softening Temp | |||
| 50℃/h | 110 | ℃ | GB/T 1633 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL-94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |