| Thermx® TE4005 NC010 is a 33% glass fiber/mineral reinforced polycyclohexylenedimethylene terephthalate resin developed for injection molding applications. It is specifically suitable for high performance demanding ignition applications. PRELIMINARY DATA&& |
| Product Description | |
|---|---|
| Supplier | Celanese |
| Generic | PCT |
| Material Status | Commercial: Active |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.45 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.52 | % | ISO 294-4 |
| MD | 0.28 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 9000 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| fracture | 110 | MPa | ISO 527-2/1A/5 |
| Tensile strain | |||
| fracture | 1.8 | % | ISO 527-2/1A/5 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 40 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 230 | ℃ | ISO 75-2/A |
| Melting temperature | 285 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | 46 | kV/mm | IEC 60243-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 95 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Recommended maximum moisture content | 0.030 | % | |
| Processing (melt) temperature | 295 to 310 | °C | |
| Mold temperature | 120 to 140 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |