| About |
|---|
| An anti-static high-viscosity grade for general extrusion molding (rods, plates, sheets, etc.) Suitable for applications requiring surface resistivity 10E9 ohm Cautions Surface resistivity will change with extrusion conditions: die design, pressure, speed, etc. In addition, color shade will change with product thickness, retention time, and annealing conditions.&& |
| Product Description | |
|---|---|
| Supplier | Korea Engineering |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | High Viscosity,Conductive,Copolymer,Antistatic property,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| MD：3.0 mm | 1.6 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 43.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| yield | 18 | % | ISO 527-2 |
| fracture | 90 | % | ISO 527-2 |
| Bending modulus | 1350 | MPa | ISO 178 |
| bending strength | 50.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 16 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 70.0 | ℃ | ISO 75-2/A |
| Melting temperature | 165 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+9 | ohms | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Hopper temperature | 60 to 80 | °C | |
| Barrel rear temperature | 170 to 180 | °C | |
| Barrel middle temperature | 180 to 190 | °C | |
| Barrel front temperature | 190 to 200 | °C | |
| Nozzle temperature | 180 to 210 | °C | |
| Mold temperature | 60 to 80 | °C | |
| Back pressure | < 2.00 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |