| About |
|---|
| Supreme™ 024, Polyolefin Plastomer (POP), is an ethylene-octene copolymer produced via Nexlene™ technology. Supreme™ 024 performs well in a wide range of various cast film applications with excellent sealing property, cling force, and impact strength. |
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | POP |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.902 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.5 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of falling darts | 850 | g | ASTM D1709A |
| Sealing starting temperature | 84 | ℃ | SK Method |
| tear strength | |||
| TD | 22 | g/µm | ASTM D1922 |
| MD | 9 | g/µm | ASTM D1922 |
| tensile strength | |||
| MD, fracture | 48 | MPa | ASTM D882 |
| tensile strength | |||
| TD, fracture | 40 | MPa | ASTM D882 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 98 | ℃ | Internal Method |
| Vicat Softening Temp | 83 | ℃ | ASTM D1525 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | ASTM D374 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | 0.5 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |