| Hostacom HYG 343L 356015 is a 40% glass fiber reinforced PP homopolymer, with very high melt flow rate, very good color stability in hot water or steam, very good hot water resistance, very high stiffness and excellent LTHS (long term heat stability). Product is UL listed. Please contact Lyondellbasell for shrinkage recommendations. Relative temperature index Mech w/Imp. The product is also available as a customized color matched, pellet form. This grade is delivered in 356015 color version. This grade is not intended for medical, pharmaceutical, food and drinking water applications.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good heat aging resistance,High liquidity,Good color stability,Homopolymer,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 26 to 36 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 25.0 to 35.0 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 9400 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, 23 ℃ | 114 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| Yield, 23 ℃ | 2.2 | % | ISO 527-2 |
| fracture | 2.5 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 9200 | MPa | ISO 178-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0℃ | 8.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| 0℃ | 45 | kJ/m² | ISO 179/1eU |
| 23℃ | 47 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 145 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 135 | ℃ | ISO 306/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 3.00 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |