| FH35 resin is a High Density Polyethylene that is designed for flat die film extrusion and shows good mechanical properties. Applications: Diapers, sanitary napkins and other specialties. Process: Cast Film Extrusion&& |
| Product Description | |
|---|---|
| Supplier | Braskem |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Inoxidizability,High density,Butylene copolymer |
| Availabilitys | Latin America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.942 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.9 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| TD, fracture, 25 µ m, blow molded film | 20.0 | MPa | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 30.0 | MPa | ASTM D882 |
| Tensile strain | |||
| TD, fracture, 25 µ m, blow molded film | 430 | % | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 1400 | % | ASTM D882 |
| Bending modulus | |||
| 1% secant, TD, 25 µ m, blow molded film | 540 | MPa | ASTM D790 |
| 1% secant, MD, 25 µ m, blow molded film | 490 | MPa | ASTM D790 |
| tear strength | |||
| TD, 25 µ m, blow molded film | 20 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 13 | g | ASTM D1922 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |