| Ultraform N 2320 U03 UNC Q600 is a rapidly freezing UV stabilized general-purpose injection molding grade.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Copolymer |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.40 | g/cm³ | ASTM D792 |
| Density | 1.40 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 7.50 | cm³/10min | ISO 1133 |
| Shrinkage rate | ISO 294-4 | ||
| MD：3.2 mm | 2.0 | % | |
| TD | 2.1 | % | ISO 294-4 |
| MD | 2.1 | % | ISO 294-4 |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.80 | % | ISO 62 |
| saturated | 0.80 | % | ASTM D570 |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | ISO 62 |
| Balance, 50% RH | 0.20 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 2600 | MPa | ISO 527-2 |
| tensile strength | ISO 527-2 | ||
| Yield, 23 ℃ | 63.0 | MPa | ASTM D638 |
| Yield, -40 ℃ | 93.0 | MPa | ISO 527-2 |
| Yield, 23 ℃ | 63.0 | MPa | ISO 527-2 |
| Yield, 80 ℃ | 33.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 9.4 | % | ISO 527-2 |
| Yield, 23 ℃ | 9.4 | % | ASTM D638 |
| Nominal tensile fracture strain | |||
| 23℃ | 30 | % | ISO 527-2 |
| Tensile Creep Modulus（1 hr） | 1800 | MPa | ISO 899-1 |
| Tensile creep modulus | |||
| 1000 hr | 1400 | MPa | ISO 899-1 |
| Bending modulus | |||
| 23℃ | 4000 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 5.0 | kJ/m² | ISO 179 |
| 23℃ | 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | ISO 179 | ||
| -30℃ | 180 | kJ/m² | ISO 179 |
| 23℃ | 200 | kJ/m² | ISO 179 |
| Impact strength of cantilever beam notch | ASTM D256 | ||
| 23℃ | 6.5 | kJ/m² | ISO 180 |
| -40℃ | 60 | J/m | ASTM D256 |
| 23℃ | 69 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 110 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 95.0 | ℃ | ISO 75-2/A |
| 0.45 MPa, unannealed | 160 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 156 | ℃ | ISO 75-2/B |
| Melting peak temperature | 166 | ℃ | ASTM D3418 |
| Melting temperature | |||
| DSC | 166 | ℃ | ISO 3146 |
| Linear coefficient of thermal expansion | |||
| MD | 1.1E-4 | 1/℃ | |
| MD | 6.0E-5 | 1/℃ | ASTM E831 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |