| Biaxially oriented polypropylene (BOPP) film with a fast seal coating on one side and an aqueous dispersion of polyvinylidene chloride (PVdC) on the other side. FFX85/100/125 are suitable for use as a single film or in laminate structures for horizontal form-fill-seal packaging especially in the bakery and cookie markets, requiring strong seals and excellent seal integrity.&& |
| Product Description | |
|---|---|
| Generic | PP Alloy |
| Material Status | Commercial: Active |
| Features | Good heat sealing,Low or no water absorption,Optical performance,Good Printability,Retention of aroma ,Low odor,Food contact compliance,Thermal viscous strength,Moisture resistance,Broad Seal Range |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Shrinkage rate | Internal Method | ||
| MD：121℃，1 min | 4.9 | % | Internal Method |
| MD：129℃，1 min | 8.6 | % | Internal Method |
| TD：121℃，1 min | 1.4 | % | Internal Method |
| TD：129℃，1 min | 2.0 | % | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | ASTM D1894 | ||
| Dynamic with oneself, PVdC/PVdC | 0.30 | ASTM D1894 | |
| With oneself – dynamic, fast sealing/fast sealing | 0.50 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Sealing emphasis | 0.19 | N/mm | Internal Method |
| Initial sealing temperature | 65.6 to 146 | ℃ | Internal Method |
| Oxygen permeability | |||
| 25℃，0% RH | 0.16 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water vapor transmittance | |||
| 38℃，90% RH | 3.6 | g/m²/24 hr | ASTM F1770 |
| film thickness | 100 | Internal Method | |
| dosage | 40.9 | m²/kg | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 100 | ASTM D2457 | |
| Haze | 2.5 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 212°F; 1secs; 60psi; Fast Seal Surface |
| 3. 0.1secs; 60psi, Fast Seal Surface |
| 4. Wide angle, 2.5° |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |