| About |
|---|
| ELTEX® PF6812AA is a metallocene LLDPE resin produced in Europe Benefits & Features ELTEX® PF6812AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties: High stiffness Good creep resistance Excellent balance between impact resistance and rigidity Very good bubble stability and easy extrudability during blown film extrusion Good optical properties Very low blocking ELTEX® PF6812AA is formulated with antioxidants. Applications ELTEX® PF6812AA has been developed for use in coextruded blown film structures particularly suitable for food packaging, hygiene or industrial applications. Its unique balance between stiffness, toughness and optical properties makes it the material of choice for the most advanced film compositions with an optimum thickness reduction. Its excellent resistance to slow crack growth also makes ELTEX® PF6812AA valuable for geomembrane applications.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good flexibility,Optical performance,Food contact compliance,Inoxidizability,Low density,Good tear strength,Copolymer,Hexene copolymers |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.932 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.3 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Tensile modulus | ISO 1184 | ||
| 1% secant, MD, 25 µ m, blow molded film | 350 | MPa | ISO 1184 |
| 1% secant, TD, 25 µ m, blow molded film | 410 | MPa | ISO 1184 |
| tensile strength | ISO 1184 | ||
| MD, yield, 25 µ m, blow molded film | 17.0 | MPa | ISO 1184 |
| TD, yield, 25 µ m, blow molded film | 19.0 | MPa | ISO 1184 |
| MD, fracture, 25 µ m, blow molded film | 60.0 | MPa | ISO 1184 |
| TD, fracture, 25 µ m, blow molded film | 55.0 | MPa | ISO 1184 |
| Tensile strain | ISO 1184 | ||
| MD, fracture, 25 µ m, blow molded film | 640 | % | ISO 1184 |
| TD, fracture, 25 µ m, blow molded film | 770 | % | ISO 1184 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 120 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 25 µ m, blow molded film | 70 | g | ASTM D1922 |
| TD: 25 µ m, blow molded film | 520 | g | ASTM D1922 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 65 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 9.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |