Ecomass® 1002ZB92

About
Ecomass® Compound 1002ZB92. Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applications. Features: High Specific Gravity, Filled Polyether Block Amide, Excellent Toughness&&

Product Description
Generic	PA12弹性体
Material Status	Commercial: Active
Features	Good flexibility,High density
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	6.90	g/cm³

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	9.00	MPa	ISO 527-2
Tensile strain
fracture	500	%	ISO 527-2
Bending modulus	200	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch	无断裂		ISO 180/A

Process Conditions
injection	Nominal value	Unit	Test method
Extrusion	Nominal value	Unit	Test method
Drying temperature – hot air dryer	65.6	°C
Drying time – hot air dryer	4.0 to 6.0	hr
Processing (melt) temperature	204 to 232	°C
Mold temperature	26.7 to 60.0	°C
Injection speed	中等偏快
Back pressure	0.103 to 0.172	MPa
Screw speed	100 to 250	rpm
Clamping force	3.4 to 5.5	kN/cm²
Cushion	6.35 to 12.7	mm
Screw length to diameter ratio	20.0:1.0
Screw compression ratio	2.5:1.0
Drying temperature	70.0	°C
Drying time	2.0 to 4.0	hr
Melt temperature	200 to 230	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.