| Stat-Rite® S-506 is a static dissipative High-Impact Polystyrene alloy. Stat-Rite® S-506 utilizes the patented Stat-Rite® inherently dissipative polymer (IDP) alloy system to enhance standard HIPS packaging sheet with a layer of clean, permanent ESD protection. Used as a skin layer, Stat-Rite® S-506 provides more consistent ESD protection than coatings and anti-stat. The Stat-Rite® skin will NOT wash off or deteriorate over time, providing reliable ESD protection for many years. FEATURES More permanent than anti-stat Provides protection for many years Cleaner than anti-stat, coatings or carbon-filled sheet More consistent than anti-stat or coatings APPLICATIONS Static dissipative layer on HIPS electronics packaging&& |
| Product Description | |
|---|---|
| Supplier | Lubrizol Advanced Materials |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | High purity,Rapid Static Decay,Electrostatic discharge protection,Good wear resistance,Durability,Antistatic property |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.07 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 210℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1380 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 20.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 85 | % | ASTM D638 |
| Bending modulus | 1380 | MPa | ASTM D790 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 75.0 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistance | |||
| 12% R.H. | 1.0E+9 | ohms·cm | ESD S11.11 |
| Surface resistivity | |||
| 50% RH | 3.0E+9 | ohms/sq | ASTM D257 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Filler | IDP Alloy |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. measured on a co-extruded ABA sheet of S506/HIPS/S506 in a 10/80/10 thickness ratio |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |