| Synprene™ X15502011208 is a customized thermoplastic elastomer compound with NSF 51 registration. Overmold Adhesion to Polypropylene&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | TPE |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.0 | g/10min | ASTM D1238 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 31.5 | kN/m | ASTM D624 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 10 seconds | 69 | ASTM D2240 | |
| tensile strength | |||
| fracture | 6.89 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 800 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Proposed maximum recycled material ratio | 20 | % | |
| Barrel rear temperature | 166 to 188 | °C | |
| Barrel middle temperature | 177 to 188 | °C | |
| Barrel front temperature | 188 to 227 | °C | |
| Nozzle temperature | 188 to 227 | °C | |
| Mold temperature | 16 to 38 | °C | |
| Back pressure | 0.00 to 0.827 | MPa | |
| Screw speed | 40 to 100 | rpm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. ± 5 Shore A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |