| DESCRIPTION: Epocast® 167-A/B epoxy syntactic is a low-density, white, two-part system designed for insert potting and edge trim bonding in light weight honeycomb applications requiring a pourable, room-temperature curable material. Epocast® 167-A/B epoxy syntactic is qualified to BMS 5-28, Type 1.&& |
| Product Description | |
|---|---|
| Supplier | Huntsman |
| Generic | 环氧树脂 |
| Material Status | Commercial: Active |
| Features | Moisture resistance,Low density |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | ASTM D1622 | ||
| — | 0.600 | g/cm³ | ASTM D1622 |
| — | 0.700 | g/cm³ | ASTM D1622 |
| — | 1.00 | g/cm³ | ASTM D1622 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Compression modulus | 2070 | MPa | ASTM D695 |
| compressive strength | |||
| 25℃ | 41.4 | MPa | ASTM D695 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | Self-extinguishing |
| Thermosetting mixed viscosity | Nominal value | Unit | Test method |
|---|---|---|---|
| 25℃ | 800 | cP | |
| 25℃ | 45000 | cP | |
| 25℃ | 20000 | cP | |
| Gelation time | |||
| 50 gms，25℃ | 0.8 to 1.2 | hr | ASTM D2471 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Lap Shear（chromic acid etched aluminum，25℃） | 10.3 | MPa | ASTM D1002 |
| Weight gain | ASTM D543 | ||
| Distilled water：25℃ | 1.0 | % | ASTM D543 |
| Mil-M-5606，hydraulic fluid：25℃ | 1.5 | % | ASTM D543 |
| Skydrol 500-A：25℃ | 3.5 | % | ASTM D543 |
| TT-S-735，Type III test fluid：25℃ | 1.0 | % | ASTM D543 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | 60.0 | ℃ | |
| Thermosetting components | |||
| resin | 按重量计算的混合比: 100 | ||
| Hardening method | 按重量计算的混合比: 15 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Resin |
| 3. System |
| 4. Hardener |
| 5. TMA |
| 6. on immersion – 24 hrs |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |