| ALTECH® PP-H A 1000/100 DS是一种聚丙烯均聚物(PP Homopoly)产品,。 它,在北美洲、欧洲或亚太地区有供货。 特性包括: 符合 REACH 标准 通过 ROHS 认证 均聚物&& |
| Product Description | |
|---|---|
| Supplier | ALBIS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Homopolymer,Resistance to detergents |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 230℃，2.16 kg | 4.00 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179-1eA |
| Charpy Unnotch Impact strength | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 61.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| B50 | 89.0 | ℃ | ISO 306 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | |||
| H358/30 | 64.0 | MPa | ISO 2039-1 |
| Tensile modulus | 1500 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 15.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 60 | % | ISO 527-2 |
| Bending modulus | 1300 | MPa | ISO 178 |
| bending strength | 37.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 80 to 100 | °C | |
| Drying time – hot air dryer | 2.0 to 3.0 | hr | |
| Processing (melt) temperature | 200 to 270 | °C | |
| Mold temperature | 20 to 70 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |