| About |
|---|
| Ryton® XE5030BL 30% glass fiber reinforced polyphenylene sulfide alloy compound provides high ductility and impact resistance along with good thermal stability.&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Ductility,Heat Stabilized |
| Availabilitys | North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.51 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.20 | % | ASTM D995 |
| TD：3.2 mm | 0.60 | % | ASTM D995 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Thermal conductivity coefficient | 0.270 | W/m/K | ASTM C177 |
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 250 | ℃ | ASTM D648 |
| Maximum operating temperature | 130 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+14 | Ω.cm | ASTM D257 |
| Surface resistance | 1.0E+16 | Ω.cm | ASTM D257 |
| Insulation strength | |||
| 22.0 | KV/mm | ASTM D149 | |
| Dielectric constant | |||
| 3.8 | 1 kHz | ASTM D150 | |
| 3.7 | 1 MHz | ASTM D150 | |
| Dissipation factor | |||
| 3.0E-3 | ASTM D150 | ||
| 9.0E-3 | ASTM D150 | ||
| Arc resistance | 124 | sec | ASTM D495 |
| Compared to the leakage tracing index | 100 | V | ASTM D3638 |
| insulation resistance | 1.0E+11 | Ω.cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75mm | V-1 | UL 94 | |
| 1.50mm | V-0 | UL 94 | |
| 3.00mm | V-0 | UL 94 | |
| Extreme oxygen index | 34 | % | ASTM D2863 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | 1.0E-3 | cm/cm／℃ | |
| Linear coefficient of thermal expansion | 2.0E-3 | cm/cm／℃ | |
| Linear coefficient of thermal expansion | 5.5E-3 | cm/cm／℃ | ASTM E831 |
| Linear coefficient of thermal expansion | 9.0E-3 | cm/cm／℃ | ASTM E831 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 86 | M 级 | ASTM D785 |
| Rockwell hardness | 110 | R 级 | ASTM D785 |
| tensile strength | |||
| 23℃ | 131 | MPa | ASTM D638 |
| Poisson’s ratio | 0.38 | ASTM E132 | |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.0 | % | ASTM D638 |
| bending strength | |||
| 23℃ | 193 | MPa | ASTM D790 |
| Bending modulus | |||
| 23℃ | 8960 | MPa | ASTM D790 |
| compressive strength | 210 | MPa | ASTM D695 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 96 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃ | 690 | J/m | ASTM D256 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |