| This metallocene medium density polyethylene is an ethylene-hexene copolymer tailored for blown film applications that require: Exceptional clarity Excellent gloss High stiffness Good toughness Typical blown film applications include: Overwrap Bakery film Stand-up pouches&& |
| Product Description | |
|---|---|
| Supplier | Chevron Phillips |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good Clarity,Good flexibility,Good surface appearance |
| Availabilitys | North America,Latin America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.933 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.90 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | 0.90 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Membrane puncture force | |||
| 25 µm | 32.0 | N | ASTM D3763 |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 25 µ m, blow molded film | 434 | MPa | ASTM D882 |
| 1% secant, TD: 25 µ m, blow molded film | 607 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 25 µ m, blow molded film | 17.0 | MPa | ASTM D882 |
| TD, yield, 25 µ m, blow molded film | 21.0 | MPa | ASTM D882 |
| MD, fracture, 25 µ m, blow molded film | 57.0 | MPa | ASTM D882 |
| TD, fracture, 25 µ m, blow molded film | 46.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 25 µ m, blow molded film | 580 | % | ASTM D882 |
| TD, fracture, 25 µ m, blow molded film | 700 | % | ASTM D882 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 80 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD: 25 µ m, blow molded film | 50 | g | ASTM D1922 |
| TD: 25 µ m, blow molded film | 400 | g | ASTM D1922 |
| Initial sealing temperature | |||
| 25 µ m, blow molded film | 120 | ℃ | ASTM F88 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Dart impact equipped with measuring instruments | |||
| 0.0254 mm, blow molded film | 1.50 | J | ASTM D3763 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60 °, 25.4 µ m, blow molded film | 130 | ASTM D2457 | |
| Haze | |||
| 25.4 µ m, blow molded film | 5.0 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Temperature at which 0.3 lb/in heat seal strength is achieved. 0.5 s dwell, 30 psi pressure, 11.8 in/min separation rate. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |