| About |
|---|
| Lustran® 288 is a very high-flow injection molding grade of ABS (acrylonitrile butadiene styrene) with good impact strength and high gloss. It is intended for use in a wide range of applications, particularly in thin-walled components for telecommunications, office equipment, consumer and other office products. FEATURES Very high flow Good impact strength High gloss UL 94 HB rated APPLICATIONS Telecommunications Office equipment Consumer and office products&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,High liquidity |
| Availabilitys | North America,Latin America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.40-0.60 | % | ASTM D995 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 30 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| impact test | 9.00 | J | ASTM D3763 |
| impact test | 40.0 | J | ASTM D3763 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 95 | ASTM D523 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50mm | HB | UL-94 | |
| 3.00mm | HB | UL-94 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 245-265 | ℃ | |
| Dew point | <=-29.0 | ℃ | |
| Clamping pressure | 30.8-61.6 | MPa | |
| buffer | <=0.635 | cm |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71.0 -77.0 | °C | |
| Drying time | 4 | Hr | |
| Water content | <=0.10 | % | |
| Injection temperature | |||
| Rear barrel temperature | 235-250 | °C | |
| Central temperature of the barrel | 240 -255 | °C | |
| Barrel front temperature | 245-260 | °C | |
| Mold temperature | 45.0-65.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 4h/80°C |
| 3. Rate B (120°C/h), Loading 1 (10 N) |
| 4. Rate B (120°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |