| About |
|---|
| XENOY X5100 is a semi-crystalline, impact modified PC-PBT blend with excellent flow. (PC+PBT-I).&& |
| Product Description | |
|---|---|
| Supplier | SABIC |
| Generic | PC + Polyester |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Good liquidity,Hypocrystalline |
| Availabilitys | Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| Tensile modulus | 2150 | MPa | ISO 527-1-2 |
| tensile strength | ISO 527-2/50 | ||
| yield | 54.0 | MPa | |
| fracture | 40.0 | MPa | |
| Tensile strain | ISO 527-2/50 | ||
| yield | 4.5 | % | |
| fracture | 50 | % | |
| Bending modulus | 2050 | MPa | ISO 178 |
| bending strength | 80.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 15 | kJ/m² | |
| 23℃ | 50 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 | ISO 179/1eU | |
| Impact strength of cantilever beam notch | ISO 180/1A | ||
| -30℃ | 18 | kJ/m² | |
| -20℃ | 20 | kJ/m² | |
| -10℃ | 35 | kJ/m² | |
| 0℃ | 40 | kJ/m² | |
| 23℃ | 45 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed, 100 mm span | 105 | ℃ | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 84.0 | ℃ | ISO 75-2/Ae |
| Vicat Softening Temp | |||
| A50 | 135 | ℃ | ISO 306/A50 |
| B50 | 117 | ℃ | ISO 306 |
| B120 | 120 | ℃ | ISO 306/B120 |
| Ball pressure test | |||
| 75℃ | Pass | IEC 60695-10-2 | |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD：23~80℃ | 8.5E-5 | 1/℃ | |
| TD：-40~40℃ | 8.0E-5 | 1/℃ | |
| Thermal conductivity coefficient | 0.20 | W/m/K | ISO 8302 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 250℃，2.16 kg | 13.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| MD | 0.70 to 1.0 | % | Internal Method |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.50 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.15 | % | |
| Apparent viscosity of melt | |||
| 260℃，1500 sec^-1 | 215 | Pa·s | ISO 11443 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 90.0 to 100 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 40.0 to 60.0 | °C | |
| Barrel rear temperature | 230 to 250 | °C | |
| Barrel middle temperature | 240 to 265 | °C | |
| Barrel front temperature | 250 to 270 | °C | |
| Nozzle temperature | 250 to 265 | °C | |
| Processing (melt) temperature | 255 to 270 | °C | |
| Mold temperature | 60.0 to 80.0 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Tensile Bar |
| 3. 0.079 in/min |
| 4. Yield |
| 5. 80*10*4 sp=62mm |
| 6. 80*10*3 sp=62mm |
| 7. 80*10*4 |
| 8. 120*10*4 mm |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |