| About |
|---|
| Polystyrene 935E: Is a super high impact polystyrene exhibiting exceptional toughness for sheet and thermoforming applications when high ductility is crucial. Application: Cups, food packaging Custom sheet and coextrusion applications General Information: This material complies with FDA requirements as described in 21 CFR §177.1640. This material holds Underwriters Laboratory recognition 94HB; see UL File E55470 at www.UL.com. Material Safety Data Sheets are available to help customers satisfy their safety needs.&& |
| Product Description | |
|---|---|
| Supplier | TOTAL |
| Generic | PS (HIPS) |
| Material Status | Commercial: Active |
| Features | Good flexibility,High impact resistance,Ductility,HB |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | |
| Melt Flow Rate | |||
| 200℃，5.0kg | 3.7 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.40 to 0.70 | % | ASTM D955 |
| Moisture | < 0.10 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1720 | MPa | ASTM D638 |
| tensile strength | 19.3 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 60 | % | ASTM D638 |
| Bending modulus | 1790 | MPa | ASTM D790 |
| bending strength | 37.9 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 130 | J/m | ASTM D256 |
| Drop hammer impact | 15.8 | J | ASTM D3029 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 97.8 | ℃ | ASTM D1525 |
| Hot deformation temperature | |||
| annealing | 91 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 60° | 80 | ASTM D523 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |