| Secomid B 30 GF BLACK MX是一种聚酰胺6（尼龙6）材料,含有的填充物为30% 玻璃纤维增强材料。 该产品在非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。 Secomid B 30 GF BLACK MX的主要特性为:阻燃/额定火焰。 |
| Product Description | |
|---|---|
| Supplier | Poliblend |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.40 to 0.80 | % | |
| Water absorption rate | |||
| 23℃，24hr | 0.80 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8200 | MPa | ISO 527-2 |
| Tensile stress (fracture) | 140 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 2.5 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 8.0 | kJ/m² | ISO 180/A |
| Notched impact strength of cantilever beam | 55 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 200 | ℃ | ISO 75-2/A |
| Continuous use temperature | 105 | ℃ | |
| Vicat Softening Temp | 220 | ℃ | ISO 306/A |
| Ball pressure test | |||
| > 165℃ | 通过 | IEC 60695-10-2 | |
| Melting temperature | 222 | ℃ | DSC |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80 mm | HB | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glowing wire flammability index | |||
| 2.0 mm | 650 | ℃ | IEC 60695-2-12 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 90 to 100 | °C | |
| Drying time | > 3.0 | hr | |
| Processing (melt) temperature | 230 to 270 | °C | |
| Mold temperature | 70 to 90 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |